Liquid lead–bismuth eutectic (LBE) can serve as a heat transfer fluid for advanced nuclear applications as well as concentrated solar power but poses corrosion challenges for the structural materials at elevated temperatures. Oxide passivation of the surfaces of these materials during exposure to liquid LBE can inhibit such material degradation. In this study, transmission electron microscopy of oxides formed on Fe-Cr-Al alloy during exposure to lowoxygenated LBE at 800C has been performed. A complex structure of the oxide film has been revealed, consisting of a homogeneous inner layer of mostly Al₂O₃ and a heterogeneous outer layer.

At elevated temperatures, heavy liquid metals and their alloys are known to create a highly corrosive environment that causes irreversible degradation of most iron-based materials. In this paper, it has been found that an appropriate concentration of oxygen in the liquid alloy can significantly reduce this issue by creating a passivating oxide scale that controls diffusion, especially if Al is present in Fe-based materials (by Al-oxide formation). However, the increase of the temperature and of oxygen content in liquid phase leads to the increase of oxygen diffusion into bulk, and to promotion of the internal Al oxidation. This can causemore » a strain in bulk near the oxide layer, due either to mismatch between the thermal expansion coefficients of the oxides and bulk material, or to misfit of the crystal lattices (bulk vs. oxides). This work investigates the strain induced into proximal bulk of a Fe-Cr-Al alloy by oxide layers formation in liquid lead-bismuth eutectic utilizing synchrotron X-ray Laue microdiffraction. Finally, it is found that internal oxidation is the most likely cause for the strain in the metal rather than thermal expansion mismatch as a two-layer problem.« less